Ultramid 8202C is a modified crystalline and low viscosity, PA6 injection molding homopolymer. It is also available in heat stabilized (Ultramid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and chemical resistance.
Applications
Ultramid 8202C is ideally suited for applications such as: furniture casters, gears, window hardware, and fittings, insulators, bushings, valves, relays, wiring devices, and other electrical components.
Ultramid® 8202C 物性表
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
|
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 比重 | 1.13 | -- | g/cm3 | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 0.90 | -- | % | |
| 吸水率 | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| 饱和 | 9.3 | -- | % | ASTM D570 |
| 饱和, 23°C | 9.3 | -- | % | ISO 62 |
| 平衡, 50% RH | 2.6 | -- | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
| 硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 洛氏硬度 (R 级) | 120 | -- | ASTM D785 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|---|---|---|---|
| 拉伸模量 | ISO 527-2 | |||
| -40°C | 4090 | -- | MPa | ISO 527-2 |
| 23°C | 3700 | 1360 | MPa | ISO 527-2 |
| 80°C | 750 | -- | MPa | ISO 527-2 |
| 120°C | 550 | -- | MPa | ISO 527-2 |
| 150°C | 445 | -- | MPa | ISO 527-2 |
| 抗张强度 | ||||
| 屈服, -40°C | 137 | 142 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 23°C | 90.0 | 48.0 | MPa | ASTM D638 |
| 屈服, 80°C | 40.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 121°C | 30.0 | 25.0 | MPa | ASTM D638 |
| 屈服, 23°C | 88.0 | 43.0 | MPa | ISO 527-2 |
| 屈服, 120°C | 30.0 | 25.0 | MPa | ISO 527-2 |
| 屈服, 150°C | 25.0 | -- | MPa | ISO 527-2 |
| 断裂, -40°C | 130 | 80.0 | MPa | ASTM D638 |
| 断裂, 23°C | 90.0 | 70.0 | MPa | ASTM D638 |
| 断裂, 80°C | 35.0 | 30.0 | MPa | ASTM D638 |
| 断裂, 121°C | 25.0 | 20.0 | MPa | ASTM D638 |
| 伸长率 | ||||
| 屈服, -40°C | 3.0 | 3.0 | % | ASTM D638 |
| 屈服, 23°C | 4.0 | 22 | % | ASTM D638, ISO 527-2 |
| 屈服, 80°C | 25 | 25 | % | ASTM D638 |
| 屈服, 121°C | 27 | 30 | % | ASTM D638 |
| 断裂, -40°C | 5.0 | 3.0 | % | ASTM D638 |
| 断裂, 23°C | 12 | > 100 | % | ASTM D638 |
| 断裂, 80°C | > 100 | > 100 | % | ASTM D638 |
| 断裂, 121°C | > 100 | > 100 | % | ASTM D638 |
| 标称拉伸断裂应变 | ISO 527-2 | |||
| -40°C | 5.0 | 3.0 | % | ISO 527-2 |
| 23°C | 7.0 | > 50 | % | ISO 527-2 |
| 80°C | > 100 | > 100 | % | ISO 527-2 |
| 120°C | > 100 | > 100 | % | ISO 527-2 |
| 弯曲模量 | ||||
| -40°C | 3370 | 4200 | MPa | ASTM D790 |
| 23°C | 3170 | 970 | MPa | ASTM D790 |
| 65°C | 600 | -- | MPa | ASTM D790 |
| 90°C | 440 | -- | MPa | ASTM D790 |
| 121°C | 385 | -- | MPa | ASTM D790 |
| 23°C | 2800 | -- | MPa | ISO 178 |
| 弯曲强度 | ||||
| -40°C | 183 | 168 | MPa | ASTM D790 |
| 23°C | 110 | 42.0 | MPa | ASTM D790 |
| 65°C | 30.0 | -- | MPa | ASTM D790 |
| 121°C | 21.0 | -- | MPa | ASTM D790 |
| 23°C | 95.0 | -- | MPa | ISO 178 |
料筒恒温：220℃
模具温度：60-100℃。模具温度很显著地影响结晶度 ，而结晶度又影响着塑件的机械特性。对于结构部件来说结晶度很重要，因此建议模具温度为80~90℃。对于薄壁的，流程较长的塑件也建议施用较高的模具温度。增大模具温度可以提高塑件的强度和刚度，但却降低了韧性。如果壁厚大于3mm，建议使用20~40℃的低温模具。对于玻璃增强材料模具温度应大于80C。
PA6 巴斯夫 8202CPA6 巴斯夫 8202C