Ultramid® 8202C HS
聚酰胺6
BASF Corporation
产品说明：
Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in pigmented versions.
Applications
Ultramid 8202C HS is generally recommended for applications such as gears, valves, fittings, insulators, bushings, slides, window hardware, wiring devices, textile components and furniture casters.
Ultramid® 8202C HS 物性表
| 基本信息 |
|
|---|
| 添加剂 | |
| 特性 | |
| 用途 | 衬套 齿轮 电气元件 阀门/阀门部件 纺织应用 家具 绝缘材料 配件
|
| 机构评级 | |
| RoHS 合规性 | |
| 外观 | |
| 形式 | |
| 加工方法 | |
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|
| 比重 | 1.13 | -- | g/cm3 | ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) | 0.90 | -- | % |
|
| 吸水率 |
|
|
|
|
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| 饱和 | 9.3 | -- | % | ASTM D570 |
| 饱和, 23°C | 9.3 | -- | % | ISO 62 |
| 平衡, 50% RH | 2.6 | -- | % | ASTM D570 |
| 平衡, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
| 硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 (R 级) | 120 | -- |
| ASTM D785 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|
| 拉伸模量 |
|
|
| ISO 527-2 |
| -40°C | 4090 | -- | MPa | ISO 527-2 |
| 23°C | 3700 | 1360 | MPa | ISO 527-2 |
| 80°C | 750 | -- | MPa | ISO 527-2 |
| 121°C | 550 | -- | MPa | ISO 527-2 |
| 抗张强度 |
|
|
|
|
| 屈服, -40°C | 137 | 142 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 23°C | 90.0 | 48.0 | MPa | ASTM D638 |
| 屈服, 80°C | 40.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 121°C | 30.0 | 25.0 | MPa | ASTM D638, ISO 527-2 |
| 屈服, 23°C | 88.0 | 43.0 | MPa | ISO 527-2 |
| 断裂, -40°C | 130 | 80.0 | MPa | ASTM D638 |
| 断裂, 23°C | 90.0 | 70.0 | MPa | ASTM D638 |
| 断裂, 80°C | 35.0 | 30.0 | MPa | ASTM D638 |
| 断裂, 121°C | 25.0 | 20.0 | MPa | ASTM D638 |
| 伸长率 |
|
|
|
|
| 屈服, -40°C | 3.0 | 3.0 | % | ASTM D638 |
| 屈服, 23°C | 4.0 | 22 | % | ASTM D638, ISO 527-2 |
| 屈服, 80°C | 25 | 25 | % | ASTM D638 |
| 屈服, 121°C | 27 | 30 | % | ASTM D638 |
| 断裂, -40°C | 5.0 | 3.0 | % | ASTM D638 |
| 断裂, 23°C | 12 | > 100 | % | ASTM D638 |
| 断裂, 80°C | > 100 | > 100 | % | ASTM D638 |
| 断裂, 121°C | > 100 | > 100 | % | ASTM D638 |
| 标称拉伸断裂应变 (23°C) | 7.0 | > 50 | % | ISO 527-2 |
| 弯曲模量 |
|
|
|
|
| -40°C | 3370 | 4200 | MPa | ASTM D790 |
| 23°C | 3170 | 970 | MPa | ASTM D790 |
| 65°C | 600 | -- | MPa | ASTM D790 |
| 90°C | 440 | -- | MPa | ASTM D790 |
| 121°C | 385 | -- | MPa | ASTM D790 |
| 23°C | 2800 | -- | MPa | ISO 178 |
| 弯曲强度 |
|
|
|
|
| -40°C | 183 | 168 | MPa | ASTM D790 |
| 23°C | 110 | 42.0 | MPa | ASTM D790 |
| 65°C | 30.0 | -- | MPa | ASTM D790 |
| 121°C | 21.0 | -- | MPa | ASTM D790 |
| 23°C | 95.0 | -- | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
|---|
| 简支梁缺口冲击强度 (23°C) | 3.5 | -- | kJ/m2 | ISO 179 |
| 简支梁无缺口冲击强度 (23°C) | 无断裂 | -- |
| ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
| ASTM D256 |
| -40°C | 32 | 21 | J/m | ASTM D256 |
| 23°C | 48 | 170 | J/m | ASTM D256 |
| Drop Impact Resistance (23°C) | 122 | > 271 | J | 内部方法 |