| 品牌 | LG |
| 货号 | 82TR |
| 用途 | 塑胶制品厂 |
| 特性级别 | 阻燃级||| |
| 牌号 | 82TR |
| 型号 | 82TR |
| 加工级别 | 注塑级||| |
| 品名 | 其它通用塑料 |
| 外形尺寸 | 25KG |
| 用途级别 | 通用级||| |
| 生产企业 | LG |
| 是否进口 | 是 |
LG SAN 82TR
Application: Products demanding high transparency such as refrigerator sleeves.
Features: SAN from LG chemical has excellent heat resistance,chemical resistance ,mechanical properties, processibility and transparency. SAN resin is widely used for production of eletric/eletronic components,automobile components and household articles.
LG SAN 82TR 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 外观 |
|
| 加工方法 |
|
| 多点数据 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | |||
| -- | 1.07 | g/cm3 | ASTM D792 |
| -- | 1070 | kg/m3 | ISO 1183 1 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 200°C/5.0 kg | 5.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 53 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 18 | g/10 min | ASTM D1238 |
| 熔体体积流动速率 (220°C/10.0 kg) | 59.9 | cm3/10min | ISO 1133 2 |
| 收缩率 - 流动 | 0.40 到 0.70 | % | ASTM D955 |
| 吸水率 (饱和) | 0.14 | % | ISO 62 3 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级) | 124 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | |||
| -- 4 | 3080 | MPa | ASTM D638 |
| -- | 3100 | MPa | ISO 527-2 5 |
| 抗张强度 | |||
| 屈服 6 | 66.7 | MPa | ASTM D638 |
| 断裂 | 64.0 | MPa | ISO 527-2 7 |
| 伸长率 | |||
| 断裂 8 | 6.0 | % | ASTM D638 |
| 断裂 | 5.0 | % | ISO 527-2 9 |
| 弯曲模量 10 | 3600 | MPa | ASTM D790 |
| 弯曲强度 11(屈服) | 108 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA 12 | ||
| -30°C | 2.00 | kJ/m2 | ISO 179/1eA |
| 23°C | 3.00 | kJ/m2 | ISO 179/1eA |
| 简支梁冲击强度 | ISO 179/1eU 13 | ||
| -30°C | 5.00 | kJ/m2 | ISO 179/1eU |
| 23°C | 13.0 | kJ/m2 | ISO 179/1eU |
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -30°C, 6.35 mm | 9.8 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 9.8 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 (1.8 MPa, 未退火, 6.35 mm) | 90.0 | °C | ASTM D648 |
| 玻璃转化温度 14 | 110 | °C | ISO 11357-2 15 |
| 维卡软化温度 | |||
| -- | 101 | °C | ASTM D1525 16 |
| 50°C/h, B (50N) | 98.4 | °C | ISO 306 17 |
| 线形膨胀系数 | ISO 11359-2 18 | ||
| 流动 | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| 横向 | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
AS（SAN）树脂简介
学名丙烯腈-苯乙烯共聚物（acrylonitrile-styrene copolymer).英文缩写为SAN或AS,也称为SAN树脂或AS树脂。由丙烯腈与苯乙烯共聚而成的高分子化合物。一般含苯乙烯15%-50%。
AS（SAN）是由丙烯腈和苯乙烯通过本体法、悬浮法或乳液法制得。透明或半透明的水白色颗粒。透明度高,一般有浅蓝色和浅黄色两种底色。相对密度1．06-1．08g/cm3，折射率1．57，平衡吸水性0．66%，热变形温度82-105℃。
AS(SAN) LG 82TRAS(SAN) LG 82TRAS(SAN) LG 82TR