TPU 拜耳优得 UH-60D20
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| -- | 51.7 | MPa | ASTM D638 |
| 100% 应变 | 13.5 | MPa | ASTM D638 |
| 300% 应变 | 31.6 | MPa | ASTM D638 |
| 伸长率 (断裂) | 400 | % | ASTM D638 |
| 弯曲模量 (23°C) | 76.0 | MPa | ASTM D790 |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮) | 5.00 | mg | ASTM D3389 |
| Modulus of Rigidity | ASTM D1053 | ||
| -50°C | 366 | MPa | ASTM D1053 |
| -40°C | 214 | MPa | ASTM D1053 |
| -20°C | 41.3 | MPa | ASTM D1053 |
| 0°C | 13.8 | MPa | ASTM D1053 |
| 23°C | 8.40 | MPa | ASTM D1053 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸*变形 (200% 应变) | 20 | % | ASTM D412 |
| 拉伸应力 | ASTM D412 | ||
| 100%应变 | 13.5 | MPa | ASTM D412 |
| 300%应变 | 31.6 | MPa | ASTM D412 |
| 抗张强度 (断裂) | 51.7 | MPa | ASTM D412 |
| 伸长率 (断裂) | 400 | % | ASTM D412 |
| 撕裂强度 | |||
| -- 1 | 118 | kN/m | ASTM D624 |
| 开裂 | 29 | kN/m | ASTM D470 |
| 压缩*变形 | ASTM D395 | ||
| 23°C, 22 hr | 36 | % | ASTM D395 |
| 70°C, 22 hr | 61 | % | ASTM D395 |
TPU塑胶原料与水口：原料就是直接从石油里面提炼出来从来没加工的料，水口是经过一次高温成型的塑料，原料的化学性能稳定，物理性能良好，水口的物理性比原料要差的多，容易脆，比较易开裂，韧性远比不上原料，它的成型次数越多它的料性就越脆。原料与水口的分辨：从颜色上来区分水口料比例大的产品易发黄发黑。水口料做不出透明产品，做普通产品水口料的比率不能大于35%,要求低的产品水口料可以到达100%。其次水口料做大产品断口位发黑。
TPU塑胶原料加工的简介：浇注系统说明，浇注系统是指模具中从注机喷嘴开始到型腔为止的塑料流动通道。浇注系统在几大系统中最为重要。设计浇注系统的基本原则﹕在满足塑料产品质量的同时 ﹐还应有利于提高成型速度来缩短成型周期。有主流道、分流道、浇口及冷料井组成。从注射机喷嘴至模具模穴的熔融塑料路径称之为流道 ,其中 ,浇口套内塑料流道称之为主流道 ,其余部分称为分流道。分流道末端通向模穴的节流孔称之为浇口 ,在不通向模穴的分流道的末端设置冷料井。